Proton dynamics in ultrathin GdO𝑥H𝑦 films for
magneto-ionics
Name
Correction sheffels-ssheff-phd-dmse-2023-thesis_ccLicense.pdf
Description
Thesis PDF
Size
7.31 MB
Format
Adobe PDF
Checksum (MD5)
a71ce369762873bfbb62224969376dd2
Name
DisclaimerCertifiedAccepted.pdf
Description
Supplementary file
Size
106.4 KB
Format
Adobe PDF
Checksum (MD5)
324b8aa1fc9e9304d40f84e36046d0ca
Author(s)
Sheffels, Sara
Advisor(s)
Beach, Geoffrey
Date Issued
June 2023
Publisher
Massachusetts Institute of Technology
Abstract
Dynamic tuning of materials properties with simple voltage control is desirable for a variety of applications, from magnetic memory, to neuromorphic computing, to solid state pixels and optical circuit components. Metal oxides can conduct ionic current, allowing their properties and those of adjacent materials to be controlled through voltage control of ion transport and electrochemical reactions. This thesis focuses on protonic defects in gadolinium oxide and gadolinium hydroxide (GdOxHy). Protons are mobile in this oxide at room temperature, and hydrogen incorporation can control a variety of materials properties, making these devices a promising platform for thin film solid state ionic devices with very simple and robust architectures. However, the proton transport and hydrogen storage properties of GdOxHy are not sufficiently well understood to determine the limits and optimal operation conditions for this material platform. Additionally, the mixed ionic and electronic conductivity of the material poses challenges for measuring these properties. This thesis sheds light on proton dynamics in nanoscale GdOxHy films in order to understand proton conductivity and hydrogen storage. The work investigates the effects of hydration and gating on the structure of GdOxHy films and devices, measures the devices' electrical and electrochemical properties, and focuses on applications in magneto-ionics, where voltage control of protons is used to toggle the magnetic properties of a ferromagnetic or ferrimagnetic layer.
MIT Department
Massachusetts Institute of Technology. Department of Materials Science and Engineering
Terms of Use
Attribution-NonCommercial 4.0 International (CC BY-NC 4.0)
Copyright retained by author(s)
Persistent DSpace Link