The dual role of coherent twin boundaries in hydrogen embrittlement
Name
Seita-2015-Dual role.pdf
Size
1.09 MB
Format
Adobe PDF
Checksum (MD5)
6245e15244c94f4f233341e2ed21722e
Author(s)
Seita, Matteo
Hanson, John Paul
Gradecak, Silvija
Demkowicz, Michael J.
Date Issued
February 2015
Journal
Nature Communications
Publisher
Nature Publishing Group
Citation
Seita, Matteo, John P. Hanson, Silvija Gradečak, and Michael J. Demkowicz. “The Dual Role of Coherent Twin Boundaries in Hydrogen Embrittlement.” Nat Comms 6 (February 5, 2015): 6164.
Version
Final published version
Abstract
Hydrogen embrittlement (HE) causes engineering alloys to fracture unexpectedly, often at considerable economic or environmental cost. Inaccurate predictions of component lifetimes arise from inadequate understanding of how alloy microstructure affects HE. Here we investigate hydrogen-assisted fracture of a Ni-base superalloy and identify coherent twin boundaries (CTBs) as the microstructural features most susceptible to crack initiation. This is a surprising result considering the renowned beneficial effect of CTBs on mechanical strength and corrosion resistance of many engineering alloys. Remarkably, we also find that CTBs are resistant to crack propagation, implying that hydrogen-assisted crack initiation and propagation are governed by distinct physical mechanisms in Ni-base alloys. This finding motivates a re-evaluation of current lifetime models in light of the dual role of CTBs. It also indicates new paths to designing materials with HE-resistant microstructures.
MIT Department
Massachusetts Institute of Technology. Department of Materials Science and Engineering
Massachusetts Institute of Technology. Department of Nuclear Science and Engineering
Terms of Use
Creative Commons Attribution
Persistent DSpace Link
DOI of Published Version
https://doi.org/10.1038/ncomms7164