Highly Stretchable, Strain Sensing Hydrogel Optical Fibers
Name
nihms832920.pdf
Size
965.25 KB
Format
Adobe PDF
Checksum (MD5)
19118c7df59d05a7a64425414bd7485b
Author(s)
Guo, Jingjing
Liu, Xinyue
Jiang, Nan
Yetisen, Ali K.
Yuk, Hyunwoo
Yang, Changxi
Khademhosseini, Ali
Zhao, Xuanhe
Yun, Seok-Hyun
Date Issued
June 2016
Journal
Advanced Materials
Publisher
Wiley Blackwell
Citation
Guo, Jingjing et al. “Highly Stretchable, Strain Sensing Hydrogel Optical Fibers.” Advanced Materials 28, 46 (October 2016): 10244–10249 © 2016 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim
Version
Author's final manuscript
Abstract
The design and fabrication of highly stretchable and tough optical fibers made of optically optimized alginate-polyacrylamide hydrogel materials in a core/clad step-index structure was reported. To characterize the swelling properties, hydrogels were fabricated at different AAm concentrations, and their weights were measured immediately after crosslinking (pre-swelling state) and later after they have been immersed in Dulbecco's Modified Eagle Medium (DMEM) at 37°C and 5% CO2 for 3 d. The weights of postswelling samples increased by a factor of 1.53 1.62 with respect to the preswelling states almost independent of the AAM concentration. First, the core was fabricated by injecting a Ca2+ containing alginate-polyacrylamide precursor solution into a platinum-cured silicone tube mold with a syringe and curing the solution by UV light irradiation. After polymerization, the core was extracted from the mold by swelling the tube in dichloromethane for 20 min. Next, the clad was formed on the core fiber by a two-step dip-coating method. The ionic cross-linking of alginate chains by Ca2+ results in high viscosity and makes it hard to dip the core and coat a cladding layer on it. Using various tube molds of different inner diameters and varying the clad dipping time, hydrogel fibers with various core and clad diameters were fabricated. The diameter of the crosslinked core when taken out of the mold is identical to the inner diameter of the mold (pre-swelling), but it increases by a factor of 1.5 1.7 at fully swollen states. The strain accuracy was ±1% in short- and long-term measurements in the moist environment, but the readout was sensitive to the variation of swelling state of the hydrogels. Keywords: absorbance spectroscopy; fiber optics; hydrogels; strain sensing
MIT Department
Massachusetts Institute of Technology. Department of Mechanical Engineering
Terms of Use
Creative Commons Attribution-Noncommercial-Share Alike
Persistent DSpace Link
DOI of Published Version
https://doi.org/10.1002/ADMA.201603160