Gas self-diffusion in different local environments of mixed-matrix membranes as a function of UiO-66-NH2 metal–organic framework loading
Name
2024_OB_Gas Self-Diffusion UiO66NH2 paper.pdf
Description
Accepted version
Size
1.18 MB
Format
Adobe PDF
Checksum (MD5)
5785e2639ae813ac313ea9d2c18d3ed4
Name
2024_OB_Gas Self-Diffusion UiO66NH2 paper SI.pdf
Description
Supporting information
Size
1.09 MB
Format
Adobe PDF
Checksum (MD5)
646c1ae8c9d39d418fb1482f85835c69
Author(s)
Boloki, Omar
Dewitt, Stephen
Hahnert, Eric T
Smith, Zachary
Vasenkov, Sergey
Date Issued
July 4, 2024
Journal
Microporous and Mesoporous Materials
Publisher
Elsevier BV
Version
Author's final manuscript
Abstract
This work focuses on quantification of microscopic self-diffusion of gas molecules in mixed-matrix membranes (MMMs) formed by dispersing UiO-66-NH2 metal–organic framework (MOF) crystals in 6FDA-Durene polyimide. Self-diffusion measurements were performed by 13C pulsed field gradient nuclear magnetic resonance (PFG NMR) for pure CO2 and CH4 with the spatial resolution in the range of 0.5–24 μm and for different MOF loadings between 12.5 and 50 weight percent. Diffusion measurements performed for each gas in the MMM with the lowest MOF loading of 12.5 weight percent yielded a single diffusivity for all measured diffusion times corresponding to a diffusion under the condition of a fast exchange between the UiO-66-NH2 crystals and the surrounding polymer phase. However, as the UiO-66-NH2 loading was increased, two molecular ensembles were observed for both CO2 and CH4: 1) an ensemble corresponding to diffusion inside UiO-66-NH2 crystals and through the MOF–polymer interfaces, and 2) an ensemble corresponding to diffusion mainly in the polymer phase of the MMMs. This behavior can be explained by the formation of MOF clusters at higher MOF loadings. Quantification of the intra-cluster diffusivity, average cluster size, and the dependence of these properties on the MOF loading are presented and discussed. The reported measurements can serve as a framework to quantify discrete microscopic diffusion characteristics and sizes of interconnected MOF clusters in MMMs as MOF loading increases to reach the desired outcome of gas percolation over a spanning MOF cluster, viz a cluster of interconnected MOF crystals spanning an entire MMM.