A precision blade mechanism for powder recoating in Selective Laser Melting
Name
1056712317-MIT.pdf
Description
Full printable version
Size
16.47 MB
Format
Adobe PDF
Checksum (MD5)
4fa021f9a4119a74b1a2ced8b54cec86
Author(s)
Weinberg, Johannes (Johannes C.)
Advisor(s)
A. John Hart.
Date Issued
2018
Publisher
Massachusetts Institute of Technology
Abstract
Selective Laser Melting (SLM) is an industrially viable means of additively manufacturing metal components with complex geometries from a wide variety of alloys. In this process, a metal powder is spread onto a build surface in a thin layer, and then the powder is selectively melted to form a cross-sectional slice of the part. This process is repeated until the part is complete. The packing density and uniformity of the powder layer are key to creating robust SLM parts. In commercial SLM equipment, the layer is spread using a moving blade or roller mechanism (the "recoater"). There is still opportunity to optimize the process and understand how powder mechanics influence the layer quality. This thesis focuses on experimental and computational methods to study powder recoating in SLM. An instrumented recoater was built with the capability to measure forces and vary important recoating parameters, such as recoating velocity, blade height and blade geometry. The instrumented recoater was then manufactured, assembled, tested and incorporated into a custom built SLM testbed at MIT. The recoater demonstrated the ability to vary the blade height with a 70 pm stroke and measure force in the milinewton range. Furthermore, angle of repose measurements were performed on powders of various size distributions and used to calibrate a model (developed by collaborators), which demonstrates the influence of cohesion on these powders. In addition, preliminary single-particle adhesion tests were performed. Together, these capabilities allow the rational development of powder spreading parameters to achieve uniform layers in SLM.
Description
Thesis: S.M., Massachusetts Institute of Technology, Department of Mechanical Engineering, 2018.
Cataloged from PDF version of thesis.
Includes bibliographical references (pages 111-117).
Subjects
Mechanical Engineering.
MIT Department
Massachusetts Institute of Technology. Department of Mechanical Engineering
Terms of Use
MIT theses are protected by copyright. They may be viewed, downloaded, or printed from this source but further reproduction or distribution in any format is prohibited without written permission.
Persistent DSpace Link