Spray Layer-by-Layer Assembled Clay Composite Thin Films as Selective Layers in Reverse Osmosis Membranes
Name
Hammond - ACS AMI Manuscript Revision - 05 17-1.pdf
Size
896.89 KB
Format
Adobe PDF
Checksum (MD5)
ecc91e4e6c4770a781ad4721c6bda84b
Author(s)
Kovacs, Jason Richard
Liu, Chaoyang
Hammond, Paula T
Date Issued
June 2015
Journal
ACS Applied Materials & Interfaces
Publisher
American Chemical Society (ACS)
Citation
Kovacs, Jason R.; Liu, Chaoyang and Hammond, Paula T. "
Version
Author's final manuscript
Abstract
Spray layer-by-layer assembled thin films containing laponite (LAP) clay exhibit effective salt barrier and water permeability properties when applied as selective layers in reverse osmosis (RO) membranes. Negatively charged LAP platelets were layered with poly(diallyldimethylammonium) (PDAC), poly(allylamine) (PAH), and poly(acrylic acid) (PAA) in bilayer and tetralayer film architectures to generate uniform films on the order of 100 nm thick that bridge a porous poly(ether sulfone) support to form novel RO membranes. Nanostructures were formed of clay layers intercalated in a polymeric matrix that introduced size-exclusion transport mechanisms into the selective layer. Thermal cross-linking of the polymeric matrix was used to increase the mechanical stability of the films and improve salt rejection by constraining swelling during operation. Maximum salt rejection of 89% was observed for the tetralayer film architecture, with an order of magnitude increase in water permeability compared to commercially available TFC-HR membranes. These clay composite thin films could serve as a high-flux alternative to current polymeric RO membranes for wastewater and brackish water treatment as well as potentially for forward osmosis applications. In general, we illustrate that by investigating the composite systems accessed using alternating layer-by-layer assembly in conjunction with complementary covalent cross-linking, it is possible to design thin film membranes with tunable transport properties for water purification applications.
MIT Department
Massachusetts Institute of Technology. Department of Chemical Engineering
Massachusetts Institute of Technology. Department of Materials Science and Engineering
Terms of Use
Article is made available in accordance with the publisher's policy and may be subject to US copyright law. Please refer to the publisher's site for terms of use.
Persistent DSpace Link
DOI of Published Version
https://doi.org/10.1021/acsami.5b01879