Careful Choices in Low Temperature Ceramic Processing and Slow Hydration Kinetics Can Affect Proton Conduction in Ceria
Name
10.1002-adfm.202009630.pdf
Size
1.8 MB
Format
Adobe PDF
Checksum (MD5)
1613f9b5e6ed8ff12bce4d9ed5e1a3ca
Author(s)
Simons, Philipp
Torres, Kierstin P.
Rupp, Jennifer L. M.
Date Issued
May 27, 2021
Journal
Advanced Functional Materials
Publisher
Wiley
Citation
Simons, P., Torres, K. P., Rupp, J. L. M., Careful Choices in Low Temperature Ceramic Processing and Slow Hydration Kinetics Can Affect Proton Conduction in Ceria. Adv. Funct. Mater. 2021, 31, 2009630.
Version
Author's final manuscript
Abstract
Low-temperature ceramic proton conductors such as ceria are important for applications ranging from sensors and resistive switches to new devices like implantable solid-oxide glucose fuel cells. Spray pyrolysis offers a promising fabrication route for proton-conducting ceria, with direct liquid-to-solid synthesis and control over crystallinity and grain size. To date, there are conflicting reports on ceria's proton conduction mechanism, particularly whether the interior contributes to proton conduction or transport occurs exclusively along a surface water layer. In this work, proton conductivity is observed in sprayed ceria thin films at 125 °C and below. Post-annealed films exhibit higher conductivity than as-deposited films of 3.3 × 10−5 S cm−1 at 25 °C, which is comparable to previous reports and ascribed to the increase in crystallinity and grain size by post-annealing. This indicates that the interior of ceria in fact contributes to proton conduction. Remarkably slow hydration kinetics of ceria are observed, with time-dependent conductivity equilibrating to 9.53 × 10−6 S cm−1 after up to 76 h. This implies kinetics may have suppressed proton conduction in previous studies, explaining the strong fluctuations in reports to date. Slow protonation kinetics must be considered when designing functional ceria ceramics, for example, in electrochemical bio-energy conversion, sensing or neuromorphic computing.
MIT Department
Massachusetts Institute of Technology. Department of Materials Science and Engineering
Massachusetts Institute of Technology. Department of Electrical Engineering and Computer Science
Terms of Use
Creative Commons Attribution-Noncommercial-Share Alike
Persistent DSpace Link
DOI of Published Version
https://doi.org/10.1002/adfm.202009630