ZnO Nanorods Grown on p-GaN Using Hydrothermal Synthesis and Its Optoelectronic Devices Application
Name
AMMNS008.pdf
Size
182.93 KB
Format
Adobe PDF
Checksum (MD5)
4a5a8105cb433a6fa1b1a1ac1f734608
Author(s)
Le, Hong Quang
Chua, Soo-Jin
Fitzgerald, Eugene A.
Loh, Kian Ping
Date Issued
January 2007
Series/Report no.
Advanced Materials for Micro- and Nano-Systems (AMMNS)
Abstract
The ZnO nanorods with the length of 1-1.5 μm
were deposited on p-GaN by hydrothermal synthesis at low temperature 100°C. The structural and optical properties of the as-grown ZnO rods were investigated by X-Ray
diffraction (XRD) and photoluminescence (PL) spectra. After annealing treatment the as-grown films in air at 600°C,
30min, and the ZnO rods showed good crystallinity and optical properties with strong UV emission at 378 nm. In addition, a sharp UV emission peak at 369.45 nm with the
FWHM 20 meV, which attributed to the bound exciton recombination, was also observed from the ZnO rods at 80K. Next, the e-beam evaporation method was used to deposit
metal contact on n-ZnO and p-GaN. Here, we use Au and Ni/Au as metal contacts for n-ZnO and p-GaN, respectively. The current-voltage characteristics of the fabricated
n-ZnO/p-GaN heterojunction revealed rectifying behavior with a leakage current of 10⁻⁸ A at -10V, a forward current 4x10⁻⁶ A at 10V bias. The heterojunction also showed a good
photoresponse, with the change of the current – voltage characteristics under ultraviolet illumination. Under UV illumination, the forward turn on voltage changed to 7.5V.
This result showed the ability to manipulate the electron transport in the ZnO based heterojunction devices.