Statistical control and experimental design for edge bead reduction in laminating process
Name
713852140-MIT.pdf
Description
Full printable version
Size
13.6 MB
Format
Adobe PDF
Checksum (MD5)
4c3bfec65626c6137d79043e47f30eac
Author(s)
Fan, Huangjia (Francis Huangjia)
Advisor(s)
David E. Hardt.
Date Issued
2010
Publisher
Massachusetts Institute of Technology
Abstract
Edge bead formation is a well-known phenomenon typically happening in the lamination due to the physics of this process. It causes the defect of high edge observed in the carton roll after the laminated carton sheets are wrapped around the roller in Company X; the affected carton sheets can no longer be fed into customers' filling machines due to the uneven surface. To address this problem, a model with process parameters and quality characteristics was built to define the lamination. Based on this model, the capability of measurement system was verified and current process capability was calculated. After that, Shewhart control charts were employed to identify the assignable causes and to bring the process to in-control state. Then, a designed experiment was conducted to find the optimal operating conditions. It was found that line speed, screw speed, die-bolt power and die-lip build-up are most likely to be subject to disturbances. In addition, diebolt power, manifold plug and deckle blade have a statistically significant impact on the edge bead formation. As a result, an out-of-control-action plan was proposed and a recipe is recommended for edge bead reduction in laminating process.
Description
Thesis (M. Eng.)--Massachusetts Institute of Technology, Dept. of Mechanical Engineering, 2010.
Cataloged from PDF version of thesis.
Includes bibliographical references (p. 77-78).
Subjects
Mechanical Engineering.
MIT Department
Massachusetts Institute of Technology. Department of Mechanical Engineering
Terms of Use
M.I.T. theses are protected by
copyright. They may be viewed from this source for any purpose, but
reproduction or distribution in any format is prohibited without written
permission. See provided URL for inquiries about permission.
copyright. They may be viewed from this source for any purpose, but
reproduction or distribution in any format is prohibited without written
permission. See provided URL for inquiries about permission.
Persistent DSpace Link