Simultaneous transverse loading and axial strain for REBCO cable tests in the SULTAN facility
Name
Hartwig_SUST.pdf
Description
Accepted version
Size
782.54 KB
Format
Adobe PDF
Checksum (MD5)
3860305a866bc70e8f5d4321e6faabd0
Author(s)
Fry, Vincent
Estrada, Jose
Michael, Philip C
Salazar, Erica E
Vieira, Rui F
Hartwig, Zachary S
Date Issued
2022
Journal
Superconductor Science and Technology
Publisher
IOP Publishing
Citation
Fry, Vincent, Estrada, Jose, Michael, Philip C, Salazar, Erica E, Vieira, Rui F et al. 2022. "Simultaneous transverse loading and axial strain for REBCO cable tests in the SULTAN facility." Superconductor Science and Technology, 35 (7).
Version
Author's final manuscript
Abstract
Abstract
We present the design and first results of an assembly that enables rare earth barium copper oxide (REBCO) superconducting cables—the VIPER cable in this work—to be tested in the SULTAN facility under the simultaneous application of transverse electromechanical loading and axial mechanical strain. The objective is to emulate the loads that a REBCO cable would experience in a three-dimensional coil but in shorter and simpler straight cables, reducing the cost, schedule, and complexity of high-fidelity conductor qualification. The assembly uses two methods for inducing axial strain in the cables. First, hydraulic jacks stretch the assembly and inserted Invar shims lock in up to ∼0.3% axial cable strain on the benchtop at room temperature. Second, the different coefficients of thermal expansion between Invar clamps and the copper cable are exploited to induce an additional ∼0.3% axial strain on the cable when the sample is cooled in the SULTAN test well from room temperature to below 50 K. Finite element analysis modeling shows that the soldered matrix of the VIPER cable transfers approximately 50%–60% of the external cable strain into the REBCO stack. The assembly was successfully employed at SULTAN, enabling two VIPER cables to be cycled 500 times at 382 kN m−1 transverse electromechanical loads with ∼0.5% mechanical strain on the cable (corresponding to ∼0.3% mechanical strain in the REBCO stacks) demonstrating critical current degradation stabilizing after 30 cycles at less than 5% and providing confidence in VIPER cables under realistic high-field magnet conditions.
We present the design and first results of an assembly that enables rare earth barium copper oxide (REBCO) superconducting cables—the VIPER cable in this work—to be tested in the SULTAN facility under the simultaneous application of transverse electromechanical loading and axial mechanical strain. The objective is to emulate the loads that a REBCO cable would experience in a three-dimensional coil but in shorter and simpler straight cables, reducing the cost, schedule, and complexity of high-fidelity conductor qualification. The assembly uses two methods for inducing axial strain in the cables. First, hydraulic jacks stretch the assembly and inserted Invar shims lock in up to ∼0.3% axial cable strain on the benchtop at room temperature. Second, the different coefficients of thermal expansion between Invar clamps and the copper cable are exploited to induce an additional ∼0.3% axial strain on the cable when the sample is cooled in the SULTAN test well from room temperature to below 50 K. Finite element analysis modeling shows that the soldered matrix of the VIPER cable transfers approximately 50%–60% of the external cable strain into the REBCO stack. The assembly was successfully employed at SULTAN, enabling two VIPER cables to be cycled 500 times at 382 kN m−1 transverse electromechanical loads with ∼0.5% mechanical strain on the cable (corresponding to ∼0.3% mechanical strain in the REBCO stacks) demonstrating critical current degradation stabilizing after 30 cycles at less than 5% and providing confidence in VIPER cables under realistic high-field magnet conditions.
MIT Department
Massachusetts Institute of Technology. Department of Nuclear Science and Engineering
Terms of Use
Creative Commons Attribution-Noncommercial-Share Alike
Persistent DSpace Link
DOI of Published Version
https://doi.org/10.1088/1361-6668/AC6BCC