Uranium from seawater research : final progress report, FY 1982
Name
10662004.pdf
Size
4.08 MB
Format
Adobe PDF
Checksum (MD5)
d3e3a8feba65debe12ccf63f25f2adea
Author(s)
Borzekowski, J.
Driscoll Michael J.
Best F. R.
Alternative Title
Seawater research, Uranium from
Date Issued
1982
Publisher
Cambridge, Mass. : Massachusetts Institute of Technology, Energy Laboratory, 1982
Series/Report no.
Energy Laboratory report (Massachusetts Institute of Technology. Energy Laboratory) ; no. MIT-EL 82-037
MITNE ; no. 254
Abstract
During the FY '82 campaign 14 new ion exchange resin formulations, prepared by the Rohm & Haas Company, were tested by MIT at the Woods Hole Oceanographic Institution. The best of these chelating resins was again of the acrylic amidoxime type; it picked up approximately 100 ppm uranium in seven days' exposure to seawater, which represents a factor of better than two improvement over thq seven-day results for the best FY '81 candidate (which saturated at roughly 100 ppm U after 30 days' exposure). Saturation was not reached and, within experimental accuracy, uranium accumulated at a constant rate over the seven-day period; it is speculated that a useful capacity of over 300 ppm U would be achieved. All resins of the styrenic amidoxime type were found to be an order of magnitude lower in their effective capacity for uranium in seawater than the best of the acrylic forms. Particle size effects, which were found to be less than expe!
cted from theoretical computations of both fluid and solid side mass transfer resistance, can not account for this difference. Scanning electron microscope examination by R & H scientists of ion exchange resin beads from beds subjected to seawater flow for 30 days in MIT's WHOI columns showed that the internal pores of the macro reticular- type resins become filled with debris (of undetermined nature and effect) during exposure.
Description
Includes bibliographical references
Final progress report; FY 1982
Persistent DSpace Link