Method for Photopolymerization 3D Printing of Recyclable Thermoplastic Polymers
Name
TumkurMahesh_prajtm_MSc_ME_2024_Thesis.pdf
Description
Thesis PDF
Size
84.44 MB
Format
Adobe PDF
Checksum (MD5)
6ca41cc3ca3884bc9eeab5f4ca5944d3
Author(s)
Tumkur Mahesh, Prajwal
Advisor(s)
Hart, A. John
Date Issued
May 2024
Publisher
Massachusetts Institute of Technology
Abstract
Conventional light-based processes used in additive manufacturing (AM), such as vat polymerization, yield non-recyclable thermoset polymers, which pose sustainability issues at scale. This thesis studies a method for photopolymerization 3D printing of the common polymers polyacrylonitrile (PAN) and polymethyl methacrylate (PMMA) to address the growing demand for low-waste production of high-resolution polymer parts with complex geometries in industrial-scale manufacturing. This new approach not only produces directly recyclable linear thermoplastic polymers but also enables the light-based printing of polymers soluble in their own monomer.
It was previously demonstrated by Chazot et al. that photo-defined layers of polyacrylonitrile (PAN) can be formed at a liquid-liquid interface; this technique was named interfacial photopolymerization (IPP). In this thesis, which focuses on multilayer 3D printing (3D-IPP), the resolution and stability of layers formed by IPP are improved using a light-absorbing dye while incorporating a water-soluble polyethylene glycol binder to improve yield, printing speed, and mechanical properties. Joint initiation using commercial water-soluble photoinitiators V-50 and LAP, along with the addition of HCL and CaCl2, further enhances printing performance by producing dense layers and reducing voids. Post-processing techniques are devised to preserve part geometry after printing, including controlled air drying, thermal post-processing with PEG infiltration, and the inclusion of compatible polymeric binders in the printing composition to minimize cracking and shrinkage. Additionally, hardware is developed to integrate the IPP process into a commercial projector-based 3D printer, demonstrating compatibility of the proposed chemistry with off-the-shelf hardware. The capability to digitally manufacture high resolution 3D structures with IPP is demonstrated and the physical properties of the resulting composite polymer are characterized. While 3D-IPP cannot yet directly rival conventional manufacturing methods, the benign aqueous chemistry as well as recyclability and circularity of produced parts offers a promising path towards sustainable and resource-efficient AM as the technology matures.
MIT Department
Massachusetts Institute of Technology. Department of Mechanical Engineering
Terms of Use
Attribution-ShareAlike 4.0 International (CC BY-SA 4.0)
Copyright retained by author(s)
Persistent DSpace Link