Hydrogen-bonded layer-by-layer assembly of poly(vinyl alcohol) and tannic acid
Name
890129979-MIT.pdf
Description
Full printable version
Size
4.01 MB
Format
Adobe PDF
Checksum (MD5)
856f01001603ea584ba9798060f006b0
Author(s)
Sample, Caitlin (Caitlin Sarah)
Advisor(s)
Michael F. Rubner.
Date Issued
2014
Publisher
Massachusetts Institute of Technology
Abstract
Hydrogen-bonded multilayer thin films containing tannic acid (TA) and poly(vinyl alcohol) (PVA) were assembled under different pH conditions, and film growth and dissolution behavior was assessed through profilometry. Optimal film growth was achieved at pH 4.0, which contrasted with uncontrollable assembly at lower pH and lack of growth at higher pH. Changes in growth behavior due to variations in the molecular weight and degree of hydrolysis of PVA, as well as the concentration of the two components, were also investigated. High molecular weight PVA resulted in thicker films than low molecular weight PVA in two cases: fully hydrolyzed PVA at a concentration of 1.0 mg/mL and partially hydrolyzed PVA at a concentration of 0.1 mg/mL. In addition, the dynamic adsorption and desorption behavior of these films was investigated using QCM-D. The QCM-D results showed that each polymer immersion step involves both the deposition and removal of mass to and from the system, with the degree of removal determining the extent to which film assembly is successful. The pH stability of the PVA/TA films was higher than other previously investigated PVA based multilayer systems, which is consistent with the high pKa value of TA of 8.5. This increased pH stability, combined with the antioxidant, antimicrobial, antimutagenic, antitumor, and antibacterial properties of TA and the biocompatibility of PVA, makes the PVA/TA system attractive for biomedical applications, including drug delivery and sensing.
Description
Thesis: S.B., Massachusetts Institute of Technology, Department of Materials Science and Engineering, 2014.
Cataloged from PDF version of thesis.
Includes bibliographical references (pages 28-30).
Subjects
Materials Science and Engineering.
MIT Department
Massachusetts Institute of Technology. Department of Materials Science and Engineering