Electroreduction of carbon dioxide to formate at high current densities using tin and tin oxide gas diffusion electrodes
Name
10800_2019_1332_ReferencePDF.pdf
Size
1.11 MB
Format
Adobe PDF
Checksum (MD5)
5067142d4e3f7dcea18b879bc6b583d1
Author(s)
Sen, Sujat
Brown, Steven M
Leonard, McLain
Brushett, Fikile R
Date Issued
July 22, 2019
Publisher
Springer Netherlands
Version
Author's final manuscript
Abstract
Abstract
We investigate tin (Sn) and tin oxide (SnO2) nanoparticle catalysts deposited on gas diffusion layers for the electrochemical reduction of carbon dioxide (CO2) to formate. The performance and durability of these electrodes was evaluated in a gas-fed electrolysis cell with a flowing liquid electrolyte stream and an integrated reference electrode. The SnO2 electrodes achieved peak current densities of 385 ± 19 mA cm−2 while the Sn electrodes achieved peak current densities of 214 ± 6 mA cm−2, both at a formate selectivity > 70%. The associated peak formate production rates of 7.4 ± 0.6 mmol m−2 s−1 (Sn) and 14.9 ± 0.8 mmol m−2 s−1 (SnO2) were demonstrated for a 1-h electrolysis and compare favorably to prior literature. Post-test analyses reveal chemical and physical changes to both cathodes during electrolysis including oxide reduction at applied potentials more negative than − 0.6 V versus RHE, nanoparticle aggregation, and catalyst layer erosion. Understanding and mitigating these decay processes is key to extending electrode lifetime without sacrificing formate generation rates or process efficiency.
Graphic abstract
MIT Department
Massachusetts Institute of Technology. Department of Chemical Engineering
Terms of Use
Creative Commons Attribution-Noncommercial-Share Alike
Persistent DSpace Link
DOI of Published Version
https://doi.org/10.1007/s10800-019-01332-z