Fabrication of high surface area ribbon electrodes for use in redox flow batteries via coaxial electrospinning
Name
069-Yadav-Ribbonelectrodes-1.pdf
Description
Accepted version
Size
1.57 MB
Format
Adobe PDF
Checksum (MD5)
9fb992bb3a14dd36160f0c2296434895
Author(s)
Yadav, Shashi
Kok, Matt DR
Forner-Cuenca, Antoni
Tenny, Kevin M
Chiang, Yet-Ming
Brushett, Fikile R
Jervis, Rhodri
Shearing, Paul R
Brett, Dan
Roberts, Edward PL
Date Issued
2021
Journal
Journal of Energy Storage
Publisher
Elsevier BV
Version
Author's final manuscript
Abstract
© 2020 A method for the preparation of electrospun with fibers possessing a ribbon-like cross-sectional shape was developed. These materials could prove beneficial as flow-through electrodes, since ribbons provide a higher surface-to-volume ratio compared to fibers, thereby providing higher reactive surface area at a given porosity. Fabrication of these materials was accomplished by electrospinning a coaxial fiber with a polystyrene core and polyacrylonitrile shell, followed by leaching of the core material leading to the collapse of the shell into a flat ribbon. The surviving shell was then carbonized to make an electrically conductive and electrochemically reactive fibrous structure. Analysis by x-ray computed tomography showed that ribbons of approximately 400 nm × 800 nm were produced, and experimental characterization revealed that they did indeed offer higher volumetric surface area than previously reported electrospun cylindrical fiber electrodes. The electrodes were characterized for various physical and transport properties and compared to commercial Freudenberg H23 carbon paper in terms of performance in a vanadium redox flow battery. The ribbon-based electrode had better performance and higher power density than commercial Freudenberg H23 electrode in the activation region, though suffered early onset of mass transfer limitations.
MIT Department
Massachusetts Institute of Technology. Department of Chemical Engineering
Massachusetts Institute of Technology. Department of Materials Science and Engineering
Terms of Use
Creative Commons Attribution-NonCommercial-NoDerivs License
Persistent DSpace Link
DOI of Published Version
https://doi.org/10.1016/j.est.2020.102079