Nanostructure stabilization and mechanical behavior of binary nanocrystalline alloys
Name
428131321-MIT.pdf
Description
Full printable version
Size
62.77 MB
Format
Adobe PDF
Checksum (MD5)
55dcab240f9e7d92df2e08a437e05df8
Author(s)
Trelewicz, Jason R
Advisor(s)
Christopher A. Schuh.
Date Issued
2009
Publisher
Massachusetts Institute of Technology
Abstract
The unique mechanical behavior of nanocrystalline metals has become of great interest in recent years, owing to both their remarkable strength and the emergence of new deformation physics at the nanoscale. Of particular interest has been the breakdown in Hall-Petch strength scaling, which is frequently attributed by atomistic simulations to a mechanistic shift to interface dominated plasticity. Experimental validation has been less abundant, primarily due to the processing challenges associated with achieving homogeneous nanocrystalline samples suitable for mechanical testing. Alloying has been proposed as a potential route to high-quality nanocrystalline metals, although choice of an appropriate alloy system, based on available thermodynamic data, remains elusive. In this thesis, we propose a thermodynamic model for nanostructure stabilization that derives from the energetic state variables characteristic of binary alloys. These modeling results motivate the study of Ni-W alloys in particular, which may be synthesized via aqueous electrodeposition, accessing grain sizes across the entire Hall-Petch breakdown regime as characterized by x-ray diffraction and transmission electron microscopy. Ambient temperature nanoindentation testing is employed to evaluate the mechanical behavior of the as-deposited alloys, assessing the nature of flow, the rate sensitivity, and pressure sensitivity of deformation, with emphasis on property inflections required to bridge the behavior of nanocrystalline metals to amorphous solids. The rate sensitivity, in particular, demonstrates an inherent dependence on nanocrystalline grain size, exhibiting a maximum in the vicinity of the Hall-Petch breakdown as a consequence of a shift to glass-like shear localization. In light of this finding, we study the Hall-Petch breakdown at high strain rates, and show that an "inverse Hall-Petch" weakening regime emerges at high rates. Additional effects from structural relaxation are investigated, and illustrated to strongly influence the strength scaling behavior and shift to inhomogeneous flow. Relaxed samples are also subjected to elevated temperature indentation tests, and the results discussed in the context of thermally-activated plasticity, thus providing a more quantitative analysis of the nanoscale deformation mechanisms.
Description
Thesis (Ph. D.)--Massachusetts Institute of Technology, Dept. of Materials Science and Engineering, February 2009.
Includes bibliographical references (leaves 131-145).
Subjects
Materials Science and Engineering.
MIT Department
Massachusetts Institute of Technology. Department of Materials Science and Engineering
Terms of Use
M.I.T. theses are protected by
copyright. They may be viewed from this source for any purpose, but
reproduction or distribution in any format is prohibited without written
permission. See provided URL for inquiries about permission.
copyright. They may be viewed from this source for any purpose, but
reproduction or distribution in any format is prohibited without written
permission. See provided URL for inquiries about permission.
Persistent DSpace Link