Nano-scale scratching in chemical-mechanical polishing
Name
246708928-MIT.pdf
Description
Full printable version
Size
21.58 MB
Format
Adobe PDF
Checksum (MD5)
6fc9b3ef4f6550cfe23cec9e63d7fb4f
Author(s)
Eusner, Thor
Advisor(s)
Jung-Hoon Chun and Nannaji Saka.
Alternative Title
Nano-scale scratching in CMP
Date Issued
2008
Publisher
Massachusetts Institute of Technology
Abstract
During the chemical-mechanical polishing (CMP) process, a critical step in the manufacture of ultra-large-scale integrated (ULSI) semiconductor devices, undesirable nano-scale scratches are formed on the surfaces being polished. As the width of the interconnect Cu lines continues to shrink to below 60 nm, and as the traditional Si02 dielectric is replaced by the compliant, lowdielectric-constant materials, scratching has emerged as a challenging problem. This thesis presents a contact mechanics based approach for modeling nano-scale scratching by the hard abrasive particles in the slurry. Single-particle models that use elastic and plastic analyses to determine both the lower- and upper-bounds for the load per particle are introduced. These bounds are established for both homogenous and composite coatings. Multi-particle models are also presented. These models use contact mechanics at the pad-particle-coating interface to relate the global parameters of CMP, such as pressure, particle radius, slurry volume fraction and the material and geometrical properties of the pad and coating, to the widths and depths of scratches in the coatings. A lower- and upper-limit for the scratch width and depth in CMP is defined. Controlled indentation and scratching experiments have been conducted using a Hysitron TriboIndenter to validate the single-particle models. Based on these experiments, the upper-bound load per particle is used to predict the widths and depths of scratches in coatings. Furthermore, polishing experiments have been conducted using a CMP tool to validate the limits. The upper-limit for the semi-width of a scratch is equal to the product of the particle radius and the square root of the ratio of pad hardness to coating hardness. For a typical CMP pad and Cu coating, this upper-limit is one-fifth of the particle radius. Based on the models and the experiments, practical solutions for mitigating scratching in CMP, especially Cu CMP, are suggested.
Description
Thesis (S.M.)--Massachusetts Institute of Technology, Dept. of Mechanical Engineering, 2008.
Includes bibliographical references (leaves 125-127).
Subjects
Mechanical Engineering.
MIT Department
Massachusetts Institute of Technology. Department of Mechanical Engineering
Terms of Use
M.I.T. theses are protected by
copyright. They may be viewed from this source for any purpose, but
reproduction or distribution in any format is prohibited without written
permission. See provided URL for inquiries about permission.
copyright. They may be viewed from this source for any purpose, but
reproduction or distribution in any format is prohibited without written
permission. See provided URL for inquiries about permission.
Persistent DSpace Link