Investigating intergranular fracture in nickel via atomistic simulations
Author(s)
Xu, Guoqiang, Ph. D. Massachusetts Institute of Technology
DownloadFull printable version (33.10Mb)
Other Contributors
Massachusetts Institute of Technology. Department of Materials Science and Engineering.
Advisor
Michael J. Demkowicz.
Terms of use
Metadata
Show full item recordAbstract
Alloys based on face-centered cubic (FCC) elements such as nickel (Ni) are among the most resistant to fracture. However, when embrittled by impurities, they lose their toughness and crack along grain boundaries. Though long known, this phenomenon remains poorly understood. In this thesis, we use large-scale molecular dynamics (MD) simulations to study the effects of grain boundaries (GBs) on various aspects of fracture properties in Ni, including intergranular fracture mechanisms, fracture toughness as well as crack healing. By performing statistical analysis on crack tip processes for fracture along different GBs, we revealed three distinct crack propagation mechanisms. For fracture along coherent twin boundary with the crack front along the [112] direction, no bond breaking is observed and crack advance is solely attributed to the slip of atoms at its tip due to the emission of dislocations. The dislocation process leads to the blunting of the crack tip. For fracture along [Sigma]265(100) symmetrical tilt GB, we discovered a new crack propagation mechanism, decohesion restrained by emission of dislocations (DRED). In it, bursts of brittle fracture initiate emission of dislocations, which pre- vent cracks from propagating more than a few nanometers in a single burst. For fracture along coherent twin boundary with the crack front along the [110] direction, crack propagates by brittle decohesion, which initiates dislocation emission in a similar way as DRED. However, the dislocation process does not arrest the crack due to the local hardening mechanism, which constraints the motion of dislocations. Using the method developed to calculate the critical energy release rate Gc from atomistic simulations, we also compared the toughness of fractures by these three mechanisms. In the course of investigating intergranular fracture, we discovered a new mechanism for crack healing in a 2D model. This mechanism relies on the generation of disclination dipoles due to GB migration, which can interact with the crack, causing it to advance or heal. We also demonstrate the healing of nanocracks in realistic 3D microstructures.
Description
Thesis: Ph. D., Massachusetts Institute of Technology, Department of Materials Science and Engineering, 2016. This electronic version was submitted by the student author. The certified thesis is available in the Institute Archives and Special Collections. Cataloged from student-submitted PDF version of thesis. Includes bibliographical references (pages 133-150).
Date issued
2016Department
Massachusetts Institute of Technology. Department of Materials Science and EngineeringPublisher
Massachusetts Institute of Technology
Keywords
Materials Science and Engineering.