2026-09-19T10:34:22Zhttps://dspace.mit.edu/server/oai/request

oai:dspace.mit.edu:1721.1/381982022-01-13T07:54:36Zcom_1721.1_7582com_1721.1_7581col_1721.1_131023

Emanuel M. Sachs. Yu, Richard Li-Chao Massachusetts Institute of Technology. Dept. of Mechanical Engineering. Massachusetts Institute of Technology. Department of Mechanical Engineering 2007-07-18T14:04:07Z 2007-07-18T14:04:07Z 1994 1994 http://hdl.handle.net/1721.1/38198 50060157 Thesis (M.S.)--Massachusetts Institute of Technology, Dept. of Mechanical Engineering, 1994. Includes bibliographical references (leaf 107). Three Dimensional Printing, a rapid prototyping technology, fabricates ceramic casting shells directly from 3-D CAD models. To create a shell, loose alumina powder in thin layers is joined by selectively depositing a colloidal silica binder. Firing fuses the silica to the alumina, and subsequent processing removes the unbound powder from the casting cavity. In some instances, it may be advantageous to perform powder removal before firing. This requires higher green strength than what is obtainable with the current binder. An alternative binder consisting of 18 vol.% colloidal silica co-dispersed with 10 vol.% acrylic emulsion in an aqueous medium was developed. The polymeric component imparts higher green strength to the part (3.6 vs. 0.4 MPa), yet decomposes during firing to minimize interference with the fusion of silica to alumina. The reduction of fired strength in samples printed with co-dispersions was less than 10%. Through designed experiments, performance of the co-dispersion was quantified by additional criteria such as shrinkage, warping, and binder stability. Average linear shrinkage in parts printed with co-dispersions was 0.05% after firing at 900°C. A simple model for warping, based on elastic response of a plate to free thermal strain, predicts that flat plates tend to warp into a paraboloid after firing. The experimental results correlated well with this prediction. by Richard Li-Chao Yu. M.S. 136 leaves eng Massachusetts Institute of Technology M.I.T. theses are protected by copyright. They may be viewed from this source for any purpose, but reproduction or distribution in any format is prohibited without written permission. See provided URL for inquiries about permission. http://dspace.mit.edu/handle/1721.1/7582 Mechanical Engineering. Development of a co-dispersion binder for the three-dimensional printing process to facilitate handling of ceramic casting shells in the green state Thesis application/pdf Publication unknown unknown <Publication xmlns="https://www.openaire.eu/cerif-profile/1.1/" id="f8660964-0e63-46dd-a25c-a40262d7bd16"> <Type xmlns="https://www.openaire.eu/cerif-profile/vocab/COAR_Publication_Types">http://purl.org/coar/resource_type/c_1843</Type> <Language>eng</Language> <Title>Development of a co-dispersion binder for the three-dimensional printing process to facilitate handling of ceramic casting shells in the green state</Title> <PublishedIn> <Publication> </Publication> </PublishedIn> <PublicationDate>1994</PublicationDate> <Authors> <Author> <DisplayName>Yu, Richard Li-Chao</DisplayName> <Affiliation> <OrgUnit> </OrgUnit> </Affiliation> </Author> </Authors> <Editors> </Editors> <Publishers> <Publisher> <DisplayName>Massachusetts Institute of Technology</DisplayName> <OrgUnit /> </Publisher> </Publishers> <License>http://dspace.mit.edu/handle/1721.1/7582</License> <Keyword>Mechanical Engineering.</Keyword> <Abstract>Three Dimensional Printing, a rapid prototyping technology, fabricates ceramic casting shells directly from 3-D CAD models. To create a shell, loose alumina powder in thin layers is joined by selectively depositing a colloidal silica binder. Firing fuses the silica to the alumina, and subsequent processing removes the unbound powder from the casting cavity. In some instances, it may be advantageous to perform powder removal before firing. This requires higher green strength than what is obtainable with the current binder. An alternative binder consisting of 18 vol.% colloidal silica co-dispersed with 10 vol.% acrylic emulsion in an aqueous medium was developed. The polymeric component imparts higher green strength to the part (3.6 vs. 0.4 MPa), yet decomposes during firing to minimize interference with the fusion of silica to alumina. The reduction of fired strength in samples printed with co-dispersions was less than 10%. Through designed experiments, performance of the co-dispersion was quantified by additional criteria such as shrinkage, warping, and binder stability. Average linear shrinkage in parts printed with co-dispersions was 0.05% after firing at 900°C. A simple model for warping, based on elastic response of a plate to free thermal strain, predicts that flat plates tend to warp into a paraboloid after firing. The experimental results correlated well with this prediction.</Abstract> <Access xmlns="http://purl.org/coar/access_right" > </Access> </Publication>