2026-09-20T08:00:16Zhttps://dspace.mit.edu/server/oai/requestoai:dspace.mit.edu:1721.1/532742022-01-13T07:54:37Zcom_1721.1_7582com_1721.1_7581col_1721.1_131022
Jacopo Buongiorno and Lin-wen Hu.
Kim, Sung Joong, Ph. D. Massachusetts Institute of Technology
Massachusetts Institute of Technology. Dept. of Nuclear Science and Engineering.
Massachusetts Institute of Technology. Department of Nuclear Science and Engineering
2010-03-25T15:24:23Z
2010-03-25T15:24:23Z
2009
2009
http://hdl.handle.net/1721.1/53274
547232274
Thesis (Ph. D.)--Massachusetts Institute of Technology, Dept. of Nuclear Science and Engineering, 2009.
Cataloged from PDF version of thesis.
Includes bibliographical references (p. 285-290).
A nanofluid is a colloidal suspension of nano-scale particles in water, or other base fluids. Previous pool boiling studies have shown that nanofluids can improve the critical heat flux (CHF) by as much as 200%. In this study, subcooled flow boiling heat transfer and CHF experiments were performed with low concentrations of alumina, zinc oxide, and diamond nanoparticles in water (< 0.1 % by volume) at atmospheric pressure. It was found that for comparable test conditions the values of the nanofluid and water heat transfer coefficient (HTC) are similar (within ±20%). The HTC increased with mass flux and heat flux for water and nanofluids alike, as expected in flow boiling. The CHF tests were conducted at 0.1 MPa and at three different mass fluxes (1500, 2000, 2500 kg/m2s) under subcooled conditions. The maximum CHF enhancement was 53%, 53% and 38% for alumina, zinc oxide and diamond, respectively, always obtained at the highest mass flux. The measurement uncertainty of the CHF was less than 6.2%. A post-mortem analysis of the boiling surface reveals that its morphology is altered by deposition of the particles during nanofluids boiling. A confocal-microscopy-based examination of the test section revealed nanoparticles deposition not only changes the number of micro-cavities on the surface, but also the surface wettability. A simple model was used to estimate the ensuing nucleation site density changes, but no definitive correlation between the nucleation site density and the heat transfer coefficient data could be found.
(cont.) Wettability of the surface was substantially increased for heater coupons boiled in alumina and zinc oxide nanofluids, and such wettability increase seems to correlate reasonably well with the observed marked CHF enhancement for the respective nanofluids. Interpretation of the experimental data was conducted in light of the governing surface parameters and existing models. It was found that no single parameter could explain the observed HTC or CHF phenomena. The existing models were limited in studying the surface effects, suggesting that more accurate models incorporating surface effects need to be developed. Finally, the research activities performed in this thesis help identify the research gaps and indicate future research directions.
by Sung Joon Kim.
Ph.D.
407 p.
eng
Massachusetts Institute of Technology
M.I.T. theses are protected by
copyright. They may be viewed from this source for any purpose, but
reproduction or distribution in any format is prohibited without written
permission. See provided URL for inquiries about permission.
http://dspace.mit.edu/handle/1721.1/7582
Nuclear Science and Engineering.
Subcooled flow boiling heat transfer and critical heat flux in water-based nanofluids at low pressure
Thesis
application/pdf
false
Publication
unknown
unknown
<Publication xmlns="https://www.openaire.eu/cerif-profile/1.1/" id="c3359972-4eb6-47d8-bc34-ce5f1eb80a59">
<Type xmlns="https://www.openaire.eu/cerif-profile/vocab/COAR_Publication_Types">http://purl.org/coar/resource_type/c_1843</Type>
<Language>eng</Language>
<Title>Subcooled flow boiling heat transfer and critical heat flux in water-based nanofluids at low pressure</Title>
<PublishedIn>
<Publication>
</Publication>
</PublishedIn>
<PublicationDate>2009</PublicationDate>
<Authors>
<Author>
<DisplayName>Kim, Sung Joong, Ph. D. Massachusetts Institute of Technology</DisplayName>
<Affiliation>
<OrgUnit>
</OrgUnit>
</Affiliation>
</Author>
</Authors>
<Editors>
</Editors>
<Publishers>
<Publisher>
<DisplayName>Massachusetts Institute of Technology</DisplayName>
<OrgUnit />
</Publisher>
</Publishers>
<License>http://dspace.mit.edu/handle/1721.1/7582</License>
<Keyword>Nuclear Science and Engineering.</Keyword>
<Abstract>A nanofluid is a colloidal suspension of nano-scale particles in water, or other base fluids. Previous pool boiling studies have shown that nanofluids can improve the critical heat flux (CHF) by as much as 200%. In this study, subcooled flow boiling heat transfer and CHF experiments were performed with low concentrations of alumina, zinc oxide, and diamond nanoparticles in water (< 0.1 % by volume) at atmospheric pressure. It was found that for comparable test conditions the values of the nanofluid and water heat transfer coefficient (HTC) are similar (within ±20%). The HTC increased with mass flux and heat flux for water and nanofluids alike, as expected in flow boiling. The CHF tests were conducted at 0.1 MPa and at three different mass fluxes (1500, 2000, 2500 kg/m2s) under subcooled conditions. The maximum CHF enhancement was 53%, 53% and 38% for alumina, zinc oxide and diamond, respectively, always obtained at the highest mass flux. The measurement uncertainty of the CHF was less than 6.2%. A post-mortem analysis of the boiling surface reveals that its morphology is altered by deposition of the particles during nanofluids boiling. A confocal-microscopy-based examination of the test section revealed nanoparticles deposition not only changes the number of micro-cavities on the surface, but also the surface wettability. A simple model was used to estimate the ensuing nucleation site density changes, but no definitive correlation between the nucleation site density and the heat transfer coefficient data could be found.</Abstract>
<Abstract>(cont.) Wettability of the surface was substantially increased for heater coupons boiled in alumina and zinc oxide nanofluids, and such wettability increase seems to correlate reasonably well with the observed marked CHF enhancement for the respective nanofluids. Interpretation of the experimental data was conducted in light of the governing surface parameters and existing models. It was found that no single parameter could explain the observed HTC or CHF phenomena. The existing models were limited in studying the surface effects, suggesting that more accurate models incorporating surface effects need to be developed. Finally, the research activities performed in this thesis help identify the research gaps and indicate future research directions.</Abstract>