Origin of residual strain in heteroepitaxial films
Author(s)
Postelnicu, Eveline; Wen, Rui-Tao; Ma, Danhao; Wang, Baoming; Wada, Kazumi; Michel, Jurgen; Kimerling, Lionel C; ... Show more Show less
DownloadPublished version (2.167Mb)
Publisher with Creative Commons License
Publisher with Creative Commons License
Creative Commons Attribution
Terms of use
Metadata
Show full item recordAbstract
Heterogeneous integration of diverse materials structures is critical to the scaling of electronic and photonic integrated circuits. For a model system of Ge-on-Si, we experimentally examine the roles of lattice misfit and thermal expansion misfit in determining the residual strain in as-grown and annealed heteroepitaxial films. We present data for Ge-on-Si growth from 400 to 730 °C followed by heat treatment from 500–900 °C. We show that strain fluctuations of 5.02% enable misfit dislocation formation, and we propose a comprehensive model for the conversion of compressive misfit strain to tensile elastic strain. The model is expressed in terms of three regimes: (1) misfit control for the low temperature growth regime at 400 °C; (2) point defect control via annealing in the point defect recovery regime at 500–650 °C; and (3) thermal expansion control for growth or anneal at T > 650 °C in the dislocation recovery regime. Growth from 400 to 730 °C exhibits near complete misfit strain relief by misfit dislocations leaving a consistent residual compressive strain of 0.09%. Growth at 400 °C followed by post growth heat treatment at 600 °C results in vertical threading dislocation density reduction via a point defect-mediated climb mechanism that gives minimal strain relief. Anneal above 650 °C promotes strain relief by dislocation glide. Temperature excursions at T > 730 °C followed by cooling to room temperature yield plastic strain in the Ge film that cannot be further relieved by thermal expansion misfit accommodation. Growth at 400–730 °C retains a residual compressive strain that represents the nucleation threshold for misfit dislocations.
Date issued
2023-09-04Department
Massachusetts Institute of Technology. Department of Materials Science and EngineeringJournal
Applied Physics Letters
Publisher
AIP Publishing
Citation
Eveline Postelnicu, Rui-Tao Wen, Danhao Ma, Baoming Wang, Kazumi Wada, Jurgen Michel, Lionel C. Kimerling; Origin of residual strain in heteroepitaxial films. Appl. Phys. Lett. 4 September 2023; 123 (10): 102103.
Version: Final published version